Independent Test Data
|
Physical Properties |
Testing Agency |
|
| Adhesion (ISO 4624) |
>5,560 psi (38.33 MPa) | The Coatings Laboratory |
| Adhesion (ASTM D 4541, elcometer pull-off) |
>3,680 psi (25.37 MPa) | The Coatings Laboratory |
| Abrasion
Resistance (ASTM D 4060,Tabor Test 1,000 cycles, CS 17 wheel, 1kg) |
10.9 milligrams loss | Technical
Inspection Services, Inc. |
| Flexibility (ASTM D 522) |
15% | The Coatings Laboratory |
| Impact
Resistance - Direct (ASTM D 2794) |
50 inch-pounds | The Coatings Laboratory |
| Impact
Resistance - Reverse (ASTM D 2794) |
13 inch-pounds | The Coatings Laboratory |
| Impact
Resistance - Direct (ASTM G 14) |
97 inch-pounds | The Coatings Laboratory |
| Static
Coefficient of Friction (ASTM D 4518-90) |
0.152 mean
static friction value |
Technical
Inspection Services, Inc. |
| Dielectric
Strength (ASTM D 149) |
>1,750 volts/mil (>68 volts/micron) | Owens-Corning
Fiberglass Corporation |
| Salt Spray (ISO 7253) |
6,000 Hours | Teknologisk Institutt |
| Cyclic Corrosion (ASTM D5894) |
Pass | The Coatings Laboratory |
| Fire Rating over
Steel (ASTM E84-91a) |
Smoke
Density-Class I Flame Spread-Class I |
Southwest
Research Institute |
| Chemical Testing (ASTM G 20 modified to 30 days at 75  F
/ 23.9C) Hydrochloric Acid in Water: pH of 2.9 Hydrofluoric Acid in Water: pH of 2.9 Sulfuric Acid in Water: pH of 2.1 NaCl (10%) + Sulfuric Acid: pH of 2.9 |
No Change No Change No Change No Change No Change No Change |
The Coatings
Laboratory |
| VOC (Volatile Organic Compounds) | 1.63 lb/gal (196 g/l) | Alpha/Owens Corning |
Note: More detailed information is available in the Summary Test Data or is available on request.